| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD297 | 1.63 | g/cm3 |
| 洛氏硬度(M级) | | ASTMD785 | 83 | |
| 肖氏硬度(邵氏A) | | ASTMD2240 | 80 | |
| 摩擦系数2 | 与自身-动态 | ASTMD1894 | 0.50 | |
| 摩擦系数2 | 与自身-静态 | ASTMD1894 | 0.80 | |
| 拉伸应力 | 50%应变 | ASTMD1414 | 3.86 | MPa |
| 拉伸应力 | 100%应变 | ASTMD1414 | 9.14 | MPa |
| 抗张强度(断裂) | | ASTMD1414 | 19.3 | MPa |
| 伸长率(断裂) | | ASTMD1414 | 230 | % |
| 撕裂强度3 | | ASTMD624 | 55.2 | kN/m |
| 压缩永久变形4 | 23°C,70hr | ASTMD395 | 19 | % |
| 压缩永久变形4 | 149°C,70hr | ASTMD395 | 36 | % |
| 压缩永久变形4 | 175°C,166hr | ASTMD395 | 40 | % |
| 压缩永久变形4 | 200°C,22hr | ASTMD395 | 27 | % |
| 压缩永久变形4 | 200°C,22hr | ASTMD395B | 40 | % |
| 压缩永久变形4 | 200°C,70hr | ASTMD395 | 34 | % |
| 压缩永久变形4 | 232°C,70hr | ASTMD395 | 39 | % |
| 压缩永久变形4 | 242°C,70hr | ASTMD395 | 22 | % |
| 压缩永久变形4 | 288°C,70hr | ASTMD395 | 64 | % |
| 空气中拉伸强度的变化率 | 149°C,70hr | ASTMD573 | 0.0 | % |
| 空气中拉伸强度的变化率 | 232°C,70hr | ASTMD573 | -10 | % |
| 空气中拉伸强度的变化率 | 276°C,70hr | ASTMD573 | -56 | % |
| 空气中拉伸强度的变化率 | 288°C,70hr | ASTMD573 | -68 | % |
| 空气中极限伸长率的变化率 | 149°C,70hr | ASTMD573 | 7.0 | % |
| 空气中极限伸长率的变化率 | 232°C,70hr | ASTMD573 | 11 | % |
| 空气中极限伸长率的变化率 | 276°C,70hr | ASTMD573 | 13 | % |
| 空气中极限伸长率的变化率 | 288°C,70hr | ASTMD573 | -22 | % |
| 空气中硬度计硬度的变化率 | 149°C,70hr | ASTMD573 | 2.0 | |
| 空气中硬度计硬度的变化率 | 232°C,70hr | ASTMD573 | -1.0 | |
| 空气中硬度计硬度的变化率 | 276°C,70hr | ASTMD573 | 0.0 | |
| 空气中硬度计硬度的变化率 | 288°C,70hr | ASTMD573 | -2.0 | |
| 拉伸强度的变化率 | 135°C,70hr,在FordATF中 | ASTMD471 | -12 | % |
| 拉伸强度的变化率 | 135°C,70hr,在Wagner21B中 | ASTMD471 | -14 | % |
| 拉伸强度的变化率 | 175°C,70hr,在Stauffer7700液体中 | ASTMD471 | -25 | % |
| 拉伸强度的变化率 | 200°C,1000hr,在Castrol325中 | ASTMD471 | -17 | % |
| 拉伸强度的变化率 | 240°C,100hr,在Castrol325中 | ASTMD471 | -22 | % |
| 拉伸强度的变化率 | 242°C,70hr,在蒸汽中5 | ASTMD471 | -44 | % |
| 极限伸长率的变化率 | 135°C,70hr,在FordATF中 | ASTMD471 | 17 | % |
| 极限伸长率的变化率 | 135°C,70hr,在Wagner21B中 | ASTMD471 | 24 | % |
| 极限伸长率的变化率 | 175°C,70hr,在Stauffer7700液体中 | ASTMD471 | 15 | % |
| 极限伸长率的变化率 | 200°C,1000hr,在Castrol325中 | ASTMD471 | 12 | % |
| 极限伸长率的变化率 | 240°C,100hr,在Castrol325中 | ASTMD471 | 25 | % |
| 极限伸长率的变化率 | 242°C,70hr,在蒸汽中5 | ASTMD471 | -32 | % |
| 硬度计硬度的变化率 | 135°C,70hr,在Wagner21B中 | ASTMD471 | -4.0 | |
| 硬度计硬度的变化率 | 175°C,70hr,在Stauffer7700液体中 | ASTMD471 | -16 | |
| 硬度计硬度的变化率 | 191°C,70hr,在FordATF中 | ASTMD471 | -7.0 | |
| 硬度计硬度的变化率 | 200°C,1000hr,inCastrol325 | ASTMD471 | -10 | |
| 硬度计硬度的变化率 | 240°C,100hr,inCastrol325 | ASTMD471 | -15 | |
| 硬度计硬度的变化率 | 242°C,70hr,inSteam5 | ASTMD471 | -2.0 | |
| 体积变化 | 135°C,70hr,在FordATF中 | ASTMD471 | 8.0 | % |
| 体积变化 | 135°C,70hr,在Wagner21B中 | ASTMD471 | 6.9 | % |
| 体积变化 | 175°C,70hr,在Stauffer7700液体中 | ASTMD471 | 25 | % |
| 体积变化 | 200°C,1000hr,在Castrol325中 | ASTMD471 | 10 | % |
| 体积变化 | 240°C,100hr,在Castrol325中 | ASTMD471 | 12 | % |
| 体积变化 | 242°C,70hr,在蒸汽中5 | ASTMD471 | 2.0 | % |
| 线形膨胀系数-流动 | | ASTME228 | 2.2E-4 | cm/cm/°C |
| ServiceTemperature | | | -5到232 | °C |
| RubberClassification | | ASTMD1418 | FEPM | |