| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD297 | 1.84 | g/cm3 |
| 洛氏硬度(M级) | | ASTMD785 | 78 | |
| 肖氏硬度(邵氏A) | | ASTMD2240 | 75 | |
| 摩擦系数2 | 与自身-动态 | ASTMD1894 | 0.50 | |
| 摩擦系数2 | 与自身-静态 | ASTMD1894 | 1.3 | |
| 拉伸应力 | 50%应变 | ASTMD412 | 2.86 | MPa |
| 拉伸应力 | 100%应变 | ASTMD412 | 6.76 | MPa |
| 抗张强度(断裂) | | ASTMD412 | 15.2 | MPa |
| 伸长率(断裂) | | ASTMD412 | 190 | % |
| 撕裂强度3 | | ASTMD624 | 34.1 | kN/m |
| 压缩永久变形 | 149°C,70hr | ASTMD395 | 6.0 | % |
| 压缩永久变形 | 150°C,22hr | ASTMD395 | 6.0 | % |
| 压缩永久变形 | 175°C,70hr4 | ASTMD395 | 16 | % |
| 压缩永久变形 | 175°C,70hr5 | ASTMD395 | 24 | % |
| 压缩永久变形 | 175°C,166hr | ASTMD395 | 24 | % |
| 压缩永久变形 | 200°C,22hr | ASTMD395 | 9.0 | % |
| 压缩永久变形 | 200°C,22hr6 | ASTMD395B | 10 | % |
| 压缩永久变形 | 200°C,70hr | ASTMD395 | 11 | % |
| 空气中拉伸强度的变化率 | 150°C,70hr | ASTMD573 | -12 | % |
| 空气中拉伸强度的变化率 | 276°C,70hr | ASTMD573 | -30 | % |
| 空气中极限伸长率的变化率 | 150°C,70hr | ASTMD573 | 6.0 | % |
| 空气中极限伸长率的变化率 | 276°C,70hr | ASTMD573 | 16 | % |
| 空气中硬度计硬度的变化率 | 150°C,70hr | ASTMD573 | 6.0 | |
| 空气中硬度计硬度的变化率 | 276°C,70hr | ASTMD573 | 6.0 | |
| 拉伸强度的变化率 | 100°C,168hr,inActuatorOil | ASTMD471 | -15 | % |
| 拉伸强度的变化率 | 100°C,168hr,inSAE10Oil | ASTMD471 | -27 | % |
| 极限伸长率的变化率 | 100°C,168hr,inActuatorOil | ASTMD471 | 1.2 | % |
| 极限伸长率的变化率 | 100°C,168hr,inSAE10Oil | ASTMD471 | -9.6 | % |
| 硬度计硬度的变化率 | 100°C,168hr,inActuatorOil | ASTMD471 | -4.0 | |
| 硬度计硬度的变化率 | 100°C,168hr,inSAE10Oil | ASTMD471 | -6.0 | |
| 体积变化 | 100°C,168hr,inActuatorOil | ASTMD471 | 3.4 | % |
| 体积变化 | 100°C,168hr,inSAE10OIL | ASTMD471 | 4.4 | % |
| 线形热膨胀系数-流动 | | ASTME228 | 2.1E-4 | cm/cm/°C |