| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD297 | 1.80 | g/cm3 |
| 洛氏硬度(M级) | | ASTMD785 | 75 | |
| 肖氏硬度(邵氏A) | | ASTMD2240 | 77 | |
| 摩擦系数2 | 与自身-动态 | ASTMD1894 | 1.1 | |
| 摩擦系数2 | 与自身-静态 | ASTMD1894 | 1.2 | |
| 拉伸应力 | 50%应变 | ASTMD412 | 2.41 | MPa |
| 拉伸应力 | 100%应变 | ASTMD412 | 6.38 | MPa |
| 抗张强度(断裂) | | ASTMD412 | 17.2 | MPa |
| 伸长率(断裂) | | ASTMD412 | 200 | % |
| 压缩永久变形3 | 24°C,70hr | ASTMD395 | 6.0 | % |
| 压缩永久变形3 | 175°C,166hr | ASTMD395 | 14 | % |
| 压缩永久变形3 | 200°C,22hr | ASTMD395 | 8.0 | % |
| 空气中拉伸强度的变化率(276°C,70hr) | | ASTMD573 | -29 | % |
| 空气中极限伸长率的变化率(276°C,70hr) | | ASTMD573 | 8.0 | % |
| 空气中硬度计硬度的变化率(邵氏A,276°C,70hr) | | ASTMD573 | -1.0 | |
| 拉伸强度的变化率 | 23°C,70hr,inReferenceOil300 | ASTMD471 | -12 | % |
| 拉伸强度的变化率 | 24°C,70hr,在基准燃料B中 | ASTMD471 | -8.0 | % |
| 拉伸强度的变化率 | 175°C,70hr,在Stauffer7700液体中 | ASTMD471 | -14 | % |
| 极限伸长率的变化率 | 23°C,70hr,inReferenceOil300 | ASTMD471 | 13 | % |
| 极限伸长率的变化率 | 24°C,70hr,在基准燃料B中 | ASTMD471 | -12 | % |
| 极限伸长率的变化率 | 175°C,70hr,在Stauffer7700液体中 | ASTMD471 | 10 | % |
| 硬度计硬度的变化率 | 支撐A,23°C,70hr,inReferenceOil300 | ASTMD471 | -6.0 | |
| 硬度计硬度的变化率 | 支撐A,24°C,70hr,inReferenceFuelB | ASTMD471 | -1.0 | |
| 硬度计硬度的变化率 | 支撐A,175°C,70hr,在Stauffer7700液体中 | ASTMD471 | -7.0 | |
| 质量变化率(276°C,70hr) | | ASTMD471 | -6.0 | % |
| 体积变化 | 23°C,70hr,inReferenceOil300 | ASTMD471 | 15 | % |
| 体积变化 | 24°C,70hr,在基准燃料B中 | ASTMD471 | 1.6 | % |
| 体积变化 | 175°C,70hr,在Stauffer7700液体中 | ASTMD471 | 15 | % |
| 线形热膨胀系数-流动 | | ASTME228 | 2.2E-4 | cm/cm/°C |
| RubberClassification | | ASTMD1418 | FKM | |
| TR10/50 | | ASTMD1329 | -31 | °C |