性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.930 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 2.0 | g/10min |
醋酸乙烯含量 | | | 9.0 | wt% |
薄膜厚度-经测试 | | | 38 | um |
TensileStrength-MD(Break,38um) | | ASTMD882 | 31.0 | MPa |
TensileStrength-TD(Break,38um) | | ASTMD882 | 27.0 | MPa |
TensileElongation-MD(Break,38um) | | ASTMD882 | 330 | % |
TensileElongation-TD(Break,38um) | | ASTMD882 | 650 | % |
落锤冲击2(38um) | | ASTMD1709 | 250 | g |
ElmendorfTearStrength-MD(38um) | | ASTMD1922 | 120 | g |
ElmendorfTearStrength-TD(38um) | | ASTMD1922 | 100 | g |
维卡软化温度 | | ASTMD1525 | 81.0 | °C |
熔融温度 | | DSC | 99.0 | °C |
Haze(38.0um) | | ASTMD1003 | 1.5 | % |