性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.925 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 1.0 | g/10min |
醋酸乙烯含量 | | | 5.0 | wt% |
SecantModulus-1%Secant,MD2(BlownFilm) | | ASTMD882 | 65.0 | MPa |
TensileStrength-MD(Yield,BlownFilm) | | ASTMD882 | 27.0 | MPa |
落锤冲击(吹塑薄膜) | | ASTMD1709A | 370 | g |
ElmendorfTearStrength-MD(BlownFilm) | | ASTMD1922 | 40 | g |
ElmendorfTearStrength-TD(BlownFilm) | | ASTMD1922 | 80 | g |
维卡软化温度 | | ASTMD1525 | 64.0 | °C |
熔融温度 | | DSC | 85.0 | °C |
光泽度(45°,吹塑薄膜) | | ASTMD2457 | 50 | |
雾度(吹塑薄膜) | | ASTMD1003 | 27 | % |