性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.952 | g/cm3 |
熔流率(熔体流动速率) | 190°C/2.16kg | ASTMD1238 | 0.050 | g/10min |
熔流率(熔体流动速率) | 190°C/21.6kg | ASTMD1238 | 8.0 | g/10min |
薄膜厚度-经测试 | | | 13 | um |
SecantModulus-1%Secant,MD | | ASTMD882 | 790 | MPa |
SecantModulus-1%Secant,TD | | ASTMD882 | 965 | MPa |
抗张强度-MD(屈服) | | ASTMD882 | 28.0 | MPa |
TensileStrength-TD(Yield) | | ASTMD882 | 26.0 | MPa |
抗张强度-MD(断裂) | | ASTMD882 | 69.0 | MPa |
抗张强度-TD(断裂) | | ASTMD882 | 41.0 | MPa |
伸长率-MD(断裂) | | ASTMD882 | 330 | % |
TensileElongation-TD(Break) | | ASTMD882 | 480 | % |
落锤冲击 | | ASTMD1709A | 280 | g |
埃尔曼多夫抗撕强度-MD | | ASTMD1922 | 20 | g |
ElmendorfTearStrength-TD | | ASTMD1922 | 200 | g |
熔融峰值温度 | | ASTMD3417 | 129 | °C |