| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重2 | | ASTMD792 | 1.19 | g/cm3 |
| 吸水率(饱和,3.18mm) | | ASTMD570 | 0.35 | % |
| 洛氏硬度(M级,3.18mm) | | ASTMD785 | 90到100 | |
| 巴氏硬度(3.18mm) | | ASTMD2583 | 48到52 | |
| 拉伸模量(3.18mm) | | ASTMD638 | 3170 | MPa |
| 抗张强度(屈服,3.18mm) | | ASTMD638 | 68.9 | MPa |
| 伸长率(断裂,3.18mm) | | ASTMD638 | 5.0 | % |
| 弯曲模量(3.18mm) | | ASTMD790 | 3100 | MPa |
| 弯曲强度(3.18mm) | | ASTMD790 | 110 | MPa |
| CharpyUnnotchedImpactStrength(3.18mm) | | ASTMD6110 | 304 | J/m |
| 悬壁梁缺口冲击强度(3.18mm) | | ASTMD256A | 21 | J/m |
| 装有测量仪表的落镖冲击3(3.18mm) | | 内部方法 | >5.42 | J |
| 载荷下热变形温度(1.8MPa,未退火,3.18mm) | | ASTMD648 | 87.8 | °C |
| 线形热膨胀系数-流动(3.18mm) | | ASTMD696 | 7.4E-5 | cm/cm/°C |
| 比热2 | | ASTMC351 | 1460 | J/kg/°C |
| 导热系数2 | | 内部方法 | 0.20 | W/m/K |
| 热稳定性4(180°C,3.18mm) | | ASTMD4802 | Nodegradation | |
| UL阻燃等级(3.2mm) | | UL94 | HB | |
| 折射率5 | | ASTMD542 | 1.490 | |
| 透射率 | 3180um6 | ASTMD1003 | 93.0 | % |
| 透射率 | 3180um7 | ASTMD1003 | 93.0 | % |
| 雾度 | 3180um6 | ASTMD1003 | 0.80 | % |
| 雾度 | 3180um7 | ASTMD1003 | <2.0 | % |
| 黄度指数7(3.18mm) | | ASTMD1925 | 0.50 | YI |
| UVTransmittance8(3.18mm) | | | <1.0 | % |
| HotFormingTemperature(3.18mm) | | 内部方法 | 160到193 | °C |