性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重3 | | ASTMD792 | 1.18 | g/cm3 |
收缩率 | 流动:3.81mm | ASTMD4802 | 2.2 | % |
收缩率 | 横向流动:3.81mm | ASTMD4802 | 1.9 | % |
吸水率(饱和,3.81mm) | | ASTMD570 | 0.30 | % |
洛氏硬度(M级,3.81mm) | | ASTMD785 | 88 | |
巴氏硬度(3.81mm) | | ASTMD2583 | 40 | |
拉伸模量(3.81mm) | | ASTMD638 | 2870 | MPa |
抗张强度(屈服,3.81mm) | | ASTMD638 | 57.0 | MPa |
伸长率(断裂,3.81mm) | | ASTMD638 | 14 | % |
弯曲模量(3.81mm) | | ASTMD790 | 2730 | MPa |
弯曲强度(3.81mm) | | ASTMD790 | 94.5 | MPa |
CharpyUnnotchedImpactStrength(3.81mm) | | ASTMD6110 | 544 | J/m |
悬壁梁缺口冲击强度(3.81mm) | | ASTMD256A | 59 | J/m |
载荷下热变形温度(1.8MPa,未退火,3.81mm) | | ASTMD648 | 80.0 | °C |
线形热膨胀系数-流动(3.81mm) | | ASTMD696 | 7.2E-5 | cm/cm/°C |
热稳定性4(180°C,3.81mm) | | ASTMD4802 | NoEffect | |
HotFormingTemperature(3.81mm) | | 内部方法 | 160到182 | °C |