| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重2 | | ASTMD792 | 1.18 | g/cm3 |
| 吸水率(饱和,4.50mm) | | ASTMD570 | 0.18 | % |
| 洛氏硬度(M级,4.50mm) | | ASTMD785 | 101 | |
| 巴氏硬度(4.50mm) | | ASTMD2583 | 54 | |
| 拉伸模量(4.50mm) | | ASTMD638 | 3250 | MPa |
| 抗张强度(屈服,4.32mm) | | ASTMD638 | 64.6 | MPa |
| 伸长率(断裂,4.50mm) | | ASTMD638 | 3.3 | % |
| 弯曲模量(4.50mm) | | ASTMD790 | 3170 | MPa |
| 弯曲强度(4.50mm) | | ASTMD790 | 120 | MPa |
| CharpyUnnotchedImpactStrength(4.50mm) | | ASTMD6110 | 315 | J/m |
| 悬壁梁缺口冲击强度(4.50mm) | | ASTMD256A | 22 | J/m |
| 载荷下热变形温度(1.8MPa,未退火,4.50mm) | | ASTMD648 | 95.6 | °C |
| 线形热膨胀系数-流动(4.50mm) | | ASTMD696 | 6.5E-5 | cm/cm/°C |
| 比热2 | | ASTMC351 | 1460 | J/kg/°C |
| 导热系数2 | | 内部方法 | 0.20 | W/m/K |
| 热稳定性3(180°C,4.50mm) | | ASTMD4802 | Nodegradation | |
| 折射率2 | | ASTMD542 | 1.490 | |
| 透射率(4500um) | | ASTMD1003 | 92.6 | % |
| 雾度(4500um) | | ASTMD1003 | 1.5 | % |
| 黄度指数(4.50mm) | | ASTMD1925 | 0.70 | YI |
| UVTransmittance4 | 280nm | | 63 | % |
| UVTransmittance4 | 300nm | | 82 | % |
| HotFormingTemperature(4.50mm) | | 内部方法 | 171到193 | °C |