| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.08 | g/cm3 |
| 密度 | | ISO1183 | 1.08 | g/cm3 |
| TensileModulus(1.91mm,CompressionMolded) | | ASTMD638 | 3.59 | MPa |
| TensileModulus(1.91mm,CompressionMolded) | | ISO527-2 | 3.59 | MPa |
| TensileStrength(Yield,1.91mm,CompressionMolded) | | ASTMD638 | 9.72 | MPa |
| TensileStress(Yield,1.91mm,CompressionMolded) | | ISO527-2 | 9.72 | MPa |
| TensileElongation(Break,1.91mm,CompressionMolded) | | ASTMD638 | 470 | % |
| TensileStrain(Break,1.91mm,CompressionMolded) | | ISO527-2 | 470 | % |
| 泰伯耐磨性(1000Cycles,1000g,CS-17转轮) | | ASTMD1044 | 7.00 | mg |
| 弹性体 | | TestMethod | NominalValue | Unit |
| 拉伸永久变形 | | ASTMD412 | 6 | % |
| TearStrength2(24°C) | | ASTMD624 | 26.3 | kN/m |
| 压缩永久变形 | 24°C,22hr | ASTMD395B | 12 | % |
| 压缩永久变形 | 100°C,22hr | ASTMD395B | 54 | % |
| 压缩永久变形 | 24°C,22hr | ISO815 | 12 | % |
| 压缩永久变形 | 100°C,22hr | ISO815 | 54 | % |
| 卡-伯模量(-50°C) | | ASTMD1043 | 68.9 | MPa |
| DurometerHardness(ShoreA,1.91mm,CompressionMolded) | | ASTMD2240 | 62 | |
| IRHD硬度 | | ISO48 | 62 | |
| 脆化温度 | | ASTMD746 | -91.1 | °C |
| 脆化温度 | | ISO974 | -91.1 | °C |
| ChangeinShoreHardnessinAir(125°C,168hr) | | ISO188 | 66 | |
| ChangeinUltimateElongation(125°C,168hr) | | ASTMD471 | 410 | % |
| ChangeinDurometerHardness(125°C,168hr) | | ASTMD471 | 66 | |
| 体积变化 | 24°C,168hr,inReferenceFuelB | ASTMD471 | 19 | % |
| 体积变化 | 100°C,168hr,inASTM#1Oil | ASTMD471 | -21 | % |
| 体积变化 | 100°C,168hr,inASTM#3Oil | ASTMD471 | 23 | % |
| 体积变化 | 100°C,168hr,在水中 | ASTMD471 | 6.0 | % |