| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.15 | g/cm3 |
| 密度 | | ISO1183 | 1.15 | g/cm3 |
| 弹性体 | | TestMethod | NominalValue | Unit |
| 拉伸应力(100%应变) | | ASTMD412 | 2.40 | MPa |
| TensileStress(100%Strain,1.90mm) | | ISO37 | 2.40 | MPa |
| TensileStrength(Break,1.90mm) | | ASTMD412 | 12.3 | MPa |
| TensileStress(Break,1.90mm) | | ISO37 | 12.3 | MPa |
| 伸长率(断裂) | | ASTMD412 | 630 | % |
| TensileElongation(Break,1.90mm) | | ISO37 | 630 | % |
| TearStrength2(24°C) | | ASTMD624 | 52.0 | kN/m |
| 压缩永久变形 | 24°C,22hr | ASTMD395 | 18 | % |
| 压缩永久变形 | 100°C,22hr | ASTMD395 | 86 | % |
| 压缩永久变形 | 24°C,22hr | ISO815 | 18 | % |
| 压缩永久变形 | 100°C,22hr | ISO815 | 86 | % |
| DurometerHardness(ShoreA,1.90mm,CompressionMolded) | | ASTMD2240 | 59 | |
| ShoreHardness(ShoreA,1.90mm,CompressionMolded) | | ISO868 | 59 | |
| 脆化温度 | | ASTMD746 | -66.0 | °C |
| 脆化温度 | | ISO812 | -66.0 | °C |