| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD471 | 1.25 | g/cm3 |
| 密度 | | ISO2781 | 1.25 | g/cm3 |
| 泰伯耐磨性(1000Cycles,1000g,CS-17转轮) | | ASTMD1044 | 5.00 | mg |
| TorsionModulus2 | -20°C,1.90mm | ASTMD1043 | 19.9 | MPa |
| TorsionModulus2 | 24°C,1.90mm | ASTMD1043 | 2.90 | MPa |
| 弹性体 | | TestMethod | NominalValue | Unit |
| 拉伸永久变形3 | | ASTMD412 | 8 | % |
| 拉伸应力 | 100%Strain,1.90mm2 | ASTMD412 | 7.90 | MPa |
| 拉伸应力 | 100%Strain,125°C,1.90mm4 | ASTMD573 | 9.40 | MPa |
| 拉伸应力 | 100%Strain,1.90mm2 | ISO37 | 7.90 | MPa |
| 拉伸应力 | 100%Strain,125°C,1.90mm4 | ISO188 | 9.40 | MPa |
| 抗张强度 | Yield,1.90mm2 | ASTMD412 | 13.1 | MPa |
| 抗张强度 | Yield,125°C,1.90mm4 | ASTMD573 | 14.0 | MPa |
| 拉伸应力 | Yield,1.90mm2 | ISO37 | 13.1 | MPa |
| 拉伸应力 | Yield,125°C,1.90mm4 | ISO188 | 14.0 | MPa |
| 伸长率 | Break,125°C,1.90mm4 | ASTMD573 | 190 | % |
| 伸长率 | Break,1.90mm2 | ASTMD412 | 210 | % |
| 伸长率 | Break,1.90mm2 | ISO37 | 210 | % |
| 伸长率 | Break,125°C,1.90mm4 | ISO188 | 190 | % |
| TearStrength5,2(1.90mm) | | ASTMD624 | 24.5 | kN/m |
| 压缩永久变形6 | 24°C,22hr | ASTMD395B | 15 | % |
| 压缩永久变形6 | 100°C,22hr | ASTMD395B | 55 | % |
| 压缩永久变形6 | 24°C,22hr | ISO815 | 15 | % |
| 压缩永久变形6 | 100°C,22hr | ISO815 | 55 | % |
| Clash-BergModulus(-30°C) | | ASTMD1043 | 68.9 | MPa |
| DurometerHardness(ShoreA,1.90mm,CompressionMolded) | | ASTMD2240 | 78 | |
| ShoreHardness(ShoreA,1.90mm,CompressionMolded) | | ISO868 | 78 | |
| 脆化温度 | | ASTMD746 | -44.0 | °C |
| 脆化温度 | | ISO812 | -44.0 | °C |
| ChangeinDurometerHardnessinAir3(ShoreA,125°C,168hr) | | ASTMD573 | -1.0 | |
| ChangeinShoreHardnessinAir3(ShoreA,125°C,168hr) | | ISO188 | -1.0 | |
| 体积变化2 | 27°C,168hr,inReferenceFuelB | ASTMD471 | 29 | % |
| 体积变化2 | 100°C,168hr,inASTM#1Oil | ASTMD471 | -8.0 | % |
| 体积变化2 | 100°C,168hr,inIRM903Oil | ASTMD471 | 23 | % |
| 体积变化2 | 100°C,168hr,在水中 | ASTMD471 | 10 | % |
| 体积变化2 | 27°C,168hr,inReferenceFuelB | ISO1817 | 29 | % |
| 体积变化2 | 100°C,168hr,inASTM#1Oil | ISO1817 | -8.0 | % |
| 体积变化2 | 100°C,168hr,inIRM903Oil | ISO1817 | 23 | % |
| 体积变化2 | 100°C,168hr,在水中 | ISO1817 | 10 | % |
| 充模分析 | | TestMethod | NominalValue | Unit |
| MeltViscosity(190°C,300sec^-1) | | ASTMD3835 | 800 | Pas |