| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 密度 | | ASTM D-1505 | 0.915 | g/cm |
| 熔融指数 | 190℃/2.16kg | ASTM D-1238 | 22 | g/10min |
| 环境应力开裂 | 10% Igepal，Rotational Molded，F50 | ASTM D-1693A | | hr |
| 环境应力开裂 | 100% Igepal，Rotational Molded，F50 | ASTM D-1693A | 1 | hr |
| 拉抻屈服强度 | 3.18mm，Rotational Molded | ASTM D-638 | 78.6 | MPa |
| 弯曲模量-1% Secant | | ASTM D-790 | 139 | MPa |
| 热变形温度 | 0.45MPa，Unannealed，Rotational Molded | ASTM D-648 | 40 | ℃ |
| 热变形温度 | 1.8MPa，Unannealed，Rotational Molded | ASTM D-648 | 23 | ℃ |