性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 0.912 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 0.90 | g/10min |
薄膜厚度-经测试 | | | 51 | um |
割线模量-1%正割,MD(51um,吹塑薄膜) | | ASTMD882 | 114 | MPa |
SecantModulus-1%Secant,TD(51um,BlownFilm) | | ASTMD882 | 123 | MPa |
TensileStrength-MD(Yield,51um,BlownFilm) | | ASTMD882 | 7.00 | MPa |
TensileStrength-TD(Yield,51um,BlownFilm) | | ASTMD882 | 7.00 | MPa |
TensileStrength-MD(Break,51um,BlownFilm) | | ASTMD882 | 49.0 | MPa |
TensileStrength-TD(Break,51um,BlownFilm) | | ASTMD882 | 54.0 | MPa |
伸长率-MD(断裂,51um,吹塑薄膜) | | ASTMD882 | 640 | % |
TensileElongation-TD(Break,51um,BlownFilm) | | ASTMD882 | 890 | % |
DartDropImpact(51um,BlownFilm) | | ASTMD1709A | >1000 | g |
ElmendorfTearStrength-MD(51um,BlownFilm) | | ASTMD1922 | 710 | g |
ElmendorfTearStrength-TD(51um,BlownFilm) | | ASTMD1922 | 1000 | g |
Gloss(45°,51.0um,BlownFilm) | | ASTMD2457 | 63 | |
Haze(51.0um,BlownFilm) | | ASTMD1003 | 8.7 | % |
补充信息 | | TestMethod | NominalValue | Unit |
LowFrictionPuncture-BlownFilm(51.0um) | | | 620 | J/cm |