性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.922 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 2.2 | g/10min |
薄膜厚度-经测试 | | | 38 | um |
可供应的薄膜厚度 | | | >25um | |
TensileStrength-MD(Yield,38um,BlownFilm) | | ASTMD882 | 10.0 | MPa |
TensileStrength-TD(Yield,38um,BlownFilm) | | ASTMD882 | 10.0 | MPa |
TensileStrength-MD(Break,38um,BlownFilm) | | ASTMD882 | 21.0 | MPa |
TensileStrength-TD(Break,38um,BlownFilm) | | ASTMD882 | 19.0 | MPa |
TensileElongation-MD(Break,38um,BlownFilm) | | ASTMD882 | 420 | % |
TensileElongation-TD(Break,38um,BlownFilm) | | ASTMD882 | 570 | % |
落锤冲击(38um,吹塑薄膜) | | ASTMD1709A | 100 | g |
ElmendorfTearStrength-MD(38um,BlownFilm) | | ASTMD1922 | 170 | g |
埃尔曼多夫抗撕强度-TD(38um,吹塑薄膜) | | ASTMD1922 | 300 | g |
Gloss(45°,38.0um,BlownFilm) | | ASTMD2457 | 73 | |
雾度(38.0um,吹塑薄膜) | | ASTMD1003 | 7.0 | % |