性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
熔融指数 | 220℃/5kg | ASTM D-1238 | 3.0 | g/10min |
熔融指数 | 220℃/10kg | ASTM D-1238 | 32.0 | g/10min |
比重 | | ASTM D-792 | 1.07 | |
变缩性 | | ASTM D-955 | 0.2-0.6 | % |
拉伸强度 | | ASTM D-638 | 750(74)(10700) | kg/cm |
伸长率 | | ASTM D-638 | 6 | % |
弯曲强度 | | ASTM D-790 | 1230(121)(17600) | kg/cm |
弯曲模数 | | ASTM D-790 | 38500(3780)(55060) | kg/cm |
IZOD冲击强度 | 63.5×12.7×6.4mm,1/4 | ASTM D-256 | 1.5(14.7)(0.3) | kg.cm/cm(J/m)(Ft*Ib/in) |
IZOD冲击强度 | 63.5×12.7×3.2mm,1/8 | ASTM D-256 | 2.0(19.6)(0.36) | kg.cm/cm(J/m)(Ft*Ib/in) |
洛氏硬度 | | ASTM D-785 | 122 | R标尺 |
HWI | | UL 746A | 3 | PLC Code |
HAI | | UL 746A | 0 | PLC Code |
HVTR | | UL 746A | 0 | PLC Code |
Arc Resistance | | ASTM D-495 | 5 | PLC Code |
CTI | | UL 746A | 1 | PLC Code |
热变形温度 | 18.5kg/cm | ASTM D-648 | 90 | ℃ |
维卡软化点 | 1000g | ASTM D-1525 | 107 | ℃ |
燃烧性 | 1/8 | UL 94 | HB | mm/min |
燃烧性 | 1/16 | UL 94 | HB | mm/min |