| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| SpecificGravity(Natural) | | ASTMD792 | 1.06 | g/cm3 |
| 密度(本色) | | ISO1183 | 1.06 | g/cm3 |
| 熔流率（熔体流动速率）(220°C/10.0kg) | | ASTMD1238 | 9.0 | g/10min |
| 熔流率（熔体流动速率）(220°C/10.0kg) | | ISO1133 | 9.0 | g/10min |
| 收缩率-流动(3.20mm) | | ASTMD955 | 0.30to0.60 | % |
| MoldingShrinkage-AcrossFlow(3.20mm) | | ASTMD955 | 0.30to0.60 | % |
| 收缩率 | 横向流量:3.20mm | ISO2577 | 0.30to0.60 | % |
| 收缩率 | 流量:3.20mm | ISO2577 | 0.30to0.60 | % |
| 吸水率(平衡,23°C) | | ASTMD570 | 0.30 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.30 | % |
| 抗张强度2(屈服) | | ASTMD638 | 41.0 | MPa |
| 拉伸应力(屈服) | | ISO527-2/50 | 48.0 | MPa |
| 伸长率2(断裂) | | ASTMD638 | 35 | % |
| 拉伸应变(断裂) | | ISO527-2/50 | 36 | % |
| 弯曲模量3 | | ASTMD790 | 2200 | MPa |
| 弯曲模量4 | | ISO178 | 2450 | MPa |
| 弯曲强度3 | | ASTMD790 | 64.0 | MPa |
| 弯曲应力4 | | ISO178 | 76.0 | MPa |
| CharpyNotchedImpactStrength5(23°C) | | ISO179/1eA | 15 | kJ/m2 |
| 悬壁梁缺口冲击强度(23°C,6.35mm) | | ASTMD256 | 190 | J/m |
| 悬壁梁缺口冲击强度5(23°C) | | ISO180/1A | 17 | kJ/m2 |
| 洛氏硬度(R级) | | ASTMD785 | 110 | |
| 洛氏硬度(R级) | | ISO2039-2 | 110 | |
| HeatDeflectionTemperature(0.45MPa,Unannealed,4.00mm) | | ISO75-2/B | 100 | °C |
| HeatDeflectionTemperature(0.45MPa,Annealed,4.00mm) | | ISO75-2/B | 108 | °C |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTMD648 | 94.0 | °C |
| HeatDeflectionTemperature(1.8MPa,Unannealed,4.00mm) | | ISO75-2/A | 86.0 | °C |
| HeatDeflectionTemperature(1.8MPa,Annealed,4.00mm) | | ISO75-2/A | 105 | °C |
| 维卡软化温度 | —— | ISO306/B50 | 106 | °C |
| 维卡软化温度 | —— | ISO306/B120 | 109 | °C |