| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| SpecificGravity(Natural) | | ASTMD792 | 1.15 | g/cm3 |
| 密度(本色) | | ISO1183 | 1.15 | g/cm3 |
| 熔流率（熔体流动速率）(200°C/5.0kg) | | ASTMD1238 | 4.0 | g/10min |
| 熔流率（熔体流动速率）(200°C/5.0kg) | | ISO1133 | 4.0 | g/10min |
| 收缩率-流动(3.20mm) | | ASTMD955 | 0.31to0.59 | % |
| MoldingShrinkage-AcrossFlow(3.20mm) | | ASTMD955 | 0.31to0.59 | % |
| 收缩率 | 横向流量:3.20mm | ISO2577 | 0.31to0.59 | % |
| 收缩率 | 流量:3.20mm | ISO2577 | 0.31to0.59 | % |
| 拉伸模量2 | | ASTMD638 | 2060 | MPa |
| 拉伸模量 | | ISO527-2/50 | 2270 | MPa |
| 抗张强度2(屈服) | | ASTMD638 | 40.5 | MPa |
| 拉伸应力(屈服) | | ISO527-2/50 | 46.0 | MPa |
| 抗张强度2(断裂) | | ASTMD638 | 31.5 | MPa |
| 拉伸应力(断裂) | | ISO527-2/50 | 34.0 | MPa |
| 伸长率2(断裂) | | ASTMD638 | 15 | % |
| 拉伸应变(断裂) | | ISO527-2/50 | 3.0 | % |
| 弯曲模量3 | | ASTMD790 | 2180 | MPa |
| 弯曲模量4 | | ISO178 | 3480 | MPa |
| 弯曲强度3 | | ASTMD790 | 60.3 | MPa |
| 弯曲应力4 | | ISO178 | 73.0 | MPa |
| CharpyNotchedImpactStrength5(23°C) | | ISO179/1eA | 20 | kJ/m2 |
| 悬壁梁缺口冲击强度 | 23°C,3.18mm | ASTMD256 | 200 | J/m |
| 悬壁梁缺口冲击强度 | 23°C,6.35mm | ASTMD256 | 210 | J/m |
| 悬壁梁缺口冲击强度5(23°C) | | ISO180/1A | 19 | kJ/m2 |
| 洛氏硬度(R级) | | ASTMD785 | 105 | |
| 洛氏硬度(R级) | | ISO2039-2 | 103 | |
| 载荷下热变形温度(0.45MPa,未退火,6.40mm) | | ASTMD648 | 85.0 | °C |
| HeatDeflectionTemperature(0.45MPa,Unannealed,4.00mm) | | ISO75-2/B | 86.0 | °C |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTMD648 | 78.0 | °C |
| HeatDeflectionTemperature(1.8MPa,Unannealed,4.00mm) | | ISO75-2/A | 70.4 | °C |
| 维卡软化温度 | | ISO306/B50 | 85.785.5 | °C |
| UL阻燃等级 | 0.8mm,Black | UL94 | V-2 | |
| UL阻燃等级 | 1.5mm | UL94 | V-1 | |
| UL阻燃等级 | 2.0mm | UL94 | V-05VB | |
| UL阻燃等级 | 3.0mm | UL94 | V-05VA | |
| UL阻燃等级 | 2.5mm | UL94 | 5VA | |