性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.938 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 0.60 | g/10min |
抗环境应力开裂(50°C,F50) | | ASTMD1693 | >10000 | hr |
肖氏硬度(邵氏D) | | ASTMD2240 | 56 | |
抗张强度2 | 屈服 | ASTMD638 | 18.6 | MPa |
抗张强度2 | 断裂 | ASTMD638 | 34.3 | MPa |
伸长率2(断裂) | | ASTMD638 | 700 | % |
弯曲模量3 | | ASTMD790 | 549 | MPa |
InternalPressureResistance | 1Hr4 | | Pass | |
InternalPressureResistance | 1000Hr5 | | Pass | |
InternalPressureResistance | 165Hr6 | | Pass | |
无缺口悬臂梁冲击(23°C,6.35mm) | | ASTMD256 | 无断裂 | |
维卡软化温度 | | ASTMD1525 | 124 | °C |
热稳定性-HydrostaticPressureTest7 | | | Pass | |