性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.900 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 1.0 | g/10min |
TensileStrength-MD(Break,50um,BlownFilm) | | ASTMD882 | 45.1 | MPa |
TensileStrength-TD(Break,50um,BlownFilm) | | ASTMD882 | 44.1 | MPa |
TensileElongation-MD(Break,50um,BlownFilm) | | ASTMD882 | 590 | % |
TensileElongation-TD(Break,50um,BlownFilm) | | ASTMD882 | 640 | % |
落锤冲击(50um,吹塑薄膜) | | ASTMD1709B | >930 | g |
始封温度2(50um,吹塑薄膜) | | InternalMethod | 92.0 | °C |
维卡软化温度 | | ASTMD1525 | 86.0 | °C |
熔融峰值温度 | | ASTMD3418 | 95.0 | °C |
光泽度(20°,50.0um,吹塑薄膜) | | ASTMD2457 | 112 | |
雾度(50.0um,吹塑薄膜) | | ASTMD1003 | 3.2 | % |