性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.919 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 3.7 | g/10min |
SecantModulus-MD(22um,CastFilm) | | ASTMD882 | 117 | MPa |
SecantModulus-TD(22um,CastFilm) | | ASTMD882 | 112 | MPa |
TensileStrength-MD(Break,22um,CastFilm) | | ASTMD882 | 45.1 | MPa |
TensileStrength-TD(Break,22um,CastFilm) | | ASTMD882 | 38.2 | MPa |
TensileElongation-MD(Break,22um,CastFilm) | | ASTMD882 | 450 | % |
TensileElongation-TD(Break,22um,CastFilm) | | ASTMD882 | 600 | % |
DartDropImpact(22um,CastFilm) | | ASTMD1709A | 500 | g |
维卡软化温度 | | ASTMD1525 | 107 | °C |
熔融峰值温度 | | ASTMD3418 | 116 | °C |
Haze(22.0um,CastFilm) | | ASTMD1003 | 0.50 | % |