性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.935 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 3.7 | g/10min |
SecantModulus-MD(22um,CastFilm) | | ASTMD882 | 178 | MPa |
SecantModulus-TD(22um,CastFilm) | | ASTMD882 | 192 | MPa |
TensileStrength-MD(Break,22um,CastFilm) | | ASTMD882 | 46.1 | MPa |
TensileStrength-TD(Break,22um,CastFilm) | | ASTMD882 | 42.2 | MPa |
TensileElongation-MD(Break,22um,CastFilm) | | ASTMD882 | 420 | % |
TensileElongation-TD(Break,22um,CastFilm) | | ASTMD882 | 550 | % |
DartDropImpact(22um,CastFilm) | | ASTMD1709A | 150 | g |
维卡软化温度 | | ASTMD1525 | 121 | °C |
熔融峰值温度 | | ASTMD3418 | 124 | °C |
Haze(22.0um,CastFilm) | | ASTMD1003 | 2.0 | % |