性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.918 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 1.5 | g/10min |
TensileStrength-MD(Break,30um,BlownFilm) | | ASTMD882 | 56.9 | MPa |
TensileStrength-TD(Break,30um,BlownFilm) | | ASTMD882 | 45.1 | MPa |
伸长率-MD(断裂,30um,吹塑薄膜) | | ASTMD882 | 580 | % |
TensileElongation-TD(Break,30um,BlownFilm) | | ASTMD882 | 620 | % |
落锤冲击(30um,吹塑薄膜) | | ASTMD1709B | 670 | g |
SealInitiationTemperature2(30um,BlownFilm) | | InternalMethod | 95.0 | °C |
弹性体 | | TestMethod | NominalValue | Unit |
撕裂强度 | 横向流量:0.0300mm | ASTMD1004 | 125 | kN/m |
撕裂强度 | 流量:0.0300mm | ASTMD1004 | 122 | kN/m |
维卡软化温度 | | ASTMD1525 | 106 | °C |
熔融峰值温度 | | ASTMD3418 | 116 | °C |
光泽度(45°,30.0um,吹塑薄膜) | | ASTMD2457 | 87 | |
雾度(30.0um,吹塑薄膜) | | ASTMD1003 | 12 | % |