性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.950 | g/cm3 |
密度 | | ISO1183 | 0.950 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 5.5to9.3 | g/10min |
熔流率(熔体流动速率)(190°C/2.16kg) | | ISO1133 | 5.5to9.3 | g/10min |
醋酸乙烯含量 | | | 23.5to26.5 | wt% |
MaleicAnhydrideContent | | | 1600 | ppm |
TensileStrength2(Break,2.80mm,CompressionMolded) | | ASTMD638 | 26.0 | MPa |
TensileStress(Break,2.80mm,CompressionMolded) | | ISO527-2/5A/50 | 26.0 | MPa |
TensileElongation2(Break,2.80mm,CompressionMolded) | | ASTMD638 | 600to900 | % |
TensileStrain(Break,2.80mm,CompressionMolded) | | ISO527-2/5A/50 | 600to900 | % |
DurometerHardness(ShoreA,2.80mm,CompressionMolded) | | ASTMD2240 | 82 | |
ShoreHardness(ShoreA,2.80mm,CompressionMolded) | | ISO868 | 82 | |
维卡软化温度 | | ASTMD15253 | 43.0 | °C |
维卡软化温度 | | ISO306/A | 43.0 | °C |
熔融温度 | | ISO11357-3 | 80.0 | °C |
RingandBallSofteningPoint | | ASTME28 | 150 | °C |