性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.25 | g/cm3 |
收缩率-流动(3.20mm) | | ASTMD955 | 0.30to0.90 | % |
TensileStrength2(Break,3.20mm) | | ASTMD638 | 118 | MPa |
伸长率2(断裂,3.20mm) | | ASTMD638 | 2.0 | % |
弯曲模量3(3.20mm) | | ASTMD790 | 8830 | MPa |
弯曲强度4(屈服,3.20mm) | | ASTMD790 | 177 | MPa |
悬壁梁缺口冲击强度(23°C,3.20mm) | | ASTMD256 | 88 | J/m |
载荷下热变形温度 | 0.45MPa,Unannealed,6.40mm4 | ASTMD648 | 260 | °C |
载荷下热变形温度 | 0.45MPa,Unannealed,6.40mm5 | ASTMD648 | 220 | °C |
介电强度(23°C,1.00mm) | | ASTMD149 | 35 | kV/mm |
漏电起痕指数(解决方案A) | | IEC60112 | 500to600 | V |
UL阻燃等级(3.0mm) | | UL94 | HB | |