| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.07 | g/cm3 |
| 密度 | | ISO11832 | 1070 | kg/m3 |
| 熔流率（熔体流动速率） | 200°C/5.0kg | ASTMD1238 | 5.0 | g/10min |
| 熔流率（熔体流动速率） | 220°C/10.0kg | ASTMD1238 | 53 | g/10min |
| 熔流率（熔体流动速率） | 230°C/3.8kg | ASTMD1238 | 18 | g/10min |
| Meltvolume-flowrate(220°C/10.0kg) | | ISO11332 | 59.9 | cm3/10min |
| 收缩率-流动 | | ASTMD955 | 0.40to0.70 | % |
| 吸水率(饱和) | | ISO622 | 0.14 | % |
| 拉伸模量3 | | ASTMD638 | 3080 | MPa |
| Tensilemodulus | | ISO527-22 | 3100 | MPa |
| 抗张强度4(屈服) | | ASTMD638 | 66.7 | MPa |
| 拉伸应力(断裂) | | ISO527-22 | 64.0 | MPa |
| 伸长率4(断裂) | | ASTMD638 | 6.0 | % |
| 拉伸应变(断裂) | | ISO527-22 | 5.0 | % |
| 弯曲模量5 | | ASTMD790 | 3600 | MPa |
| FlexuralStrength5(Yield) | | ASTMD790 | 108 | MPa |
| Charpynotchedimpactstrength(23°C) | | ISO179/1eA2 | 3.00 | kJ/m2 |
| 简支梁缺口冲击强度(-30°C) | | ISO179/1eA2 | 2.00 | kJ/m2 |
| 简支梁冲击强度(23°C) | | ISO179/1eU2 | 13.0 | kJ/m2 |
| Charpyimpactstrength(-30°C) | | ISO179/1eU2 | 5.00 | kJ/m2 |
| 悬壁梁缺口冲击强度 | -30°C,6.35mm | ASTMD256 | 9.8 | J/m |
| 悬壁梁缺口冲击强度 | 23°C,6.35mm | ASTMD256 | 9.8 | J/m |
| 洛氏硬度(R级) | | ASTMD785 | 124 | |
| 载荷下热变形温度(1.8MPa,未退火,6.35mm) | | ASTMD648 | 90.0 | °C |
| 玻璃转化温度8 | | ISO11357-22 | 110 | °C |
| 维卡软化温度 | | ASTMD15257 | 101 | °C |
| 维卡软化温度(50°C/h,B(50N)) | | ISO3062 | 98.4 | °C |
| 线形热膨胀系数-流动 | | ISO11359-22 | 6.7E-5 | cm/cm/°C |
| 线形热膨胀系数-横向 | | ISO11359-22 | 6.7E-5 | cm/cm/°C |
| RTIElec | | UL746 | 50.0 | °C |
| RTIImp | | UL746 | 50.0 | °C |
| RTIStr | | UL746 | 50.0 | °C |
| Surfaceresistivity | | IEC600932 | >1.0E+15 | ohms |
| Volumeresistivity | | IEC600932 | >1.0E+13 | ohmsm |
| UL阻燃等级 | 1.6mm | UL94 | HB | |
| UL阻燃等级 | 3.2mm | UL94 | HB | |
| BurningBehav.atthicknessh(3.20mm,UL) | | ISO12102 | HB | |