| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.45 | g/cm3 |
| 密度 | | ISO1183 | 1.45 | g/cm3 |
| 溶化体积流率（MVR）(250°C/2.16kg) | | ISO1133 | 30.0 | cm3/10min |
| 收缩率-流动(3.18mm) | | | 0.15 | % |
| 吸水率(饱和) | | ASTMD570 | 0.40 | % |
| 吸水率(饱和,23°C) | | ISO62 | 0.40 | % |
| WaterAbsorption(Equilibrium,50%RH) | | ASTMD570 | 0.25 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.25 | % |
| ViscosityNumber(ReducedViscosity) | | ISO1628 | 122.0 | ml/g |
| 拉伸模量(23°C) | | ISO527-2 | 3000 | MPa |
| 抗张强度(屈服,23°C) | | ASTMD638 | 65.0 | MPa |
| 拉伸应力(屈服,23°C) | | ISO527-2 | 65.0 | MPa |
| 伸长率(屈服,23°C) | | ASTMD638 | 3.9 | % |
| 拉伸应变(屈服,23°C) | | ISO527-2 | 3.9 | % |
| 标称拉伸断裂应变 | -40°C | ISO527-2 | 3.3 | % |
| 标称拉伸断裂应变 | 23°C | ISO527-2 | 3.5 | % |
| TensileCreepModulus(1hr) | | ISO899-1 | 1800 | MPa |
| 简支梁缺口冲击强度 | -30°C | ISO179 | 4.0 | kJ/m2 |
| 简支梁缺口冲击强度 | 23°C | ISO179 | 4.0 | kJ/m2 |
| 简支梁无缺口冲击强度(23°C) | | ISO179 | 50 | kJ/m2 |
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 37 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 37 | J/m |
| 载荷下热变形温度(0.45MPa,未退火) | | ASTMD648 | 165 | °C |
| 热变形温度(0.45MPa,未退火) | | ISO75-2/B | 170 | °C |
| 载荷下热变形温度(1.8MPa,未退火) | | ASTMD648 | 80.0 | °C |
| 热变形温度(1.8MPa,未退火) | | ISO75-2/A | 60.0 | °C |
| 熔融峰值温度 | | ASTMD3418 | 223 | °C |
| 溶融温度（DSC） | | ISO3146 | 223 | °C |
| 线形热膨胀系数-流动 | | ASTME831 | 9.0E-5 | cm/cm/°C |
| 线形热膨胀系数-流动 | | | 5.5E-5 | cm/cm/°C |
| RTIElec | 0.75mm | UL746 | 125 | °C |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| RTIElec | 3.0mm | UL746 | 125 | °C |
| RTIImp | 0.75mm | UL746 | 130 | °C |
| RTIImp | 1.5mm | UL746 | 130 | °C |
| RTIImp | 3.0mm | UL746 | 130 | °C |
| RTIStr | 0.75mm | UL746 | 140 | °C |
| RTIStr | 1.5mm | UL746 | 140 | °C |
| RTIStr | 3.0mm | UL746 | 140 | °C |
| SurfaceResistivity(1.50mm) | | ASTMD257 | 1.0E+13 | ohms |
| 表面电阻率 | | IEC60093 | 1.0E+13 | ohms |
| VolumeResistivity(1.50mm) | | ASTMD257 | >1.0E+15 | ohmscm |
| 体积电阻率 | | IEC60093 | >1.0E+15 | ohmscm |
| 介电常数 | 100Hz | IEC60250 | 3.30 | |
| 介电常数 | 1MHz | IEC60250 | 3.30 | |
| 耗散因数 | 100Hz | IEC60250 | 0.011 | |
| 耗散因数 | 1MHz | IEC60250 | 0.017 | |
| 漏电起痕指数 | | IEC60112 | 250 | V |
| UL阻燃等级 | 0.40mm | UL94 | V-0 | |
| UL阻燃等级 | 0.75mm | UL94 | V-0 | |
| UL阻燃等级 | 1.5mm | UL94 | V-0 | |
| UL阻燃等级 | 3.0mm | UL94 | V-0 | |