| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 门尼粘度(ML1+4,100°C) | | ASTMD1646 | 25到3367 | MU |
| 肖氏硬度 | 邵氏A | ASTMD2240 | 79 | |
| 肖氏硬度 | 邵氏A,1秒,6.00mm2 | ASTMD2240 | 59 | |
| 抗磨损性-Sandpaper | | ISO4649 | 132 | mm3 |
| 拉伸应力 | 100%应变 | ASTMD412 | 7.10 | MPa |
| 拉伸应力 | 100%应变2 | ASTMD412 | 2.60 | MPa |
| 拉伸应力 | 100%应变,150°C3 | ASTMD412 | 2.60 | MPa |
| 拉伸应力 | 100%应变,160°C4 | ASTMD412 | 2.20 | MPa |
| 抗张强度 | 屈服 | ASTMD412 | 18.1 | MPa |
| 抗张强度 | 屈服2 | ASTMD412 | 15.5 | MPa |
| 伸长率 | 断裂 | ASTMD412 | 260 | % |
| 伸长率 | 断裂2 | ASTMD412 | 380 | % |
| 撕裂强度 | —— | ISO34-1 | 24 | kN/m |
| 撕裂强度 | ——5,2 | ISO34-1 | 6.3 | kN/m |
| 压缩永久变形 | 23°C,94hr | VWPV3307 | 30 | % |
| 压缩永久变形 | 150°C,70hr6 | ASTMD395 | 15 | % |
| 压缩永久变形 | 150°C,94hr | VWPV3307 | 49 | % |
| 压缩永久变形 | 150°C,168hr6 | ASTMD395 | 17 | % |
| 压缩永久变形 | 150°C,168hr2 | ASTMD395 | 26 | % |
| 压缩永久变形 | 175°C,70hr6 | ASTMD395 | 25 | % |
| 压缩永久变形 | 175°C,70hr2 | ASTMD395 | 17 | % |
| 压缩永久变形 | 175°C,1008hr6 | ASTMD395 | 54 | % |
| 压缩永久变形 | 190°C,70hr6 | ASTMD395 | 30 | % |
| 空气中拉伸强度的变化率 | 175°C,504hr | ASTMD573 | -21 | % |
| 空气中拉伸强度的变化率 | 100%应变,175°C,504hr | ASTMD573 | 13 | % |
| 空气中拉伸强度的变化率 | 190°C,168hr | ASTMD573 | -21 | % |
| 空气中拉伸强度的变化率 | 100%应变,190°C,168hr | ASTMD573 | 6.0 | % |
| 空气中极限伸长率的变化率 | 175°C,504hr | ASTMD573 | -20 | % |
| 空气中极限伸长率的变化率 | 190°C,168hr | ASTMD573 | -24 | % |
| 空气中硬度计硬度的变化率 | 邵氏A,175°C,504hr | ASTMD573 | 0.0 | |
| 空气中硬度计硬度的变化率 | 邵氏A,190°C,168hr | ASTMD573 | -1.0 | |
| 拉伸强度的变化率 | 150°C,168hr,DexronVI | ASTMD471 | -25 | % |
| 拉伸强度的变化率 | 160°C,504hr,LubrizolOS206304，5W40 | ASTMD471 | -34 | % |
| 极限伸长率的变化率 | 150°C,168hr,DexronVI | ASTMD471 | -43 | % |
| 极限伸长率的变化率 | 160°C,504hr,LubrizolOS206304，5W40 | ASTMD471 | -30 | % |
| 硬度计硬度的变化率 | 支撐A,150°C,168hr,在DexronVI中 | ASTMD471 | -6.0 | |
| 硬度计硬度的变化率 | 支撐A,160°C,504hr,在LubrizolOS206304、5W40中 | ASTMD471 | -8.0 | |
| 质量变化率 | 150°C,168hr,在DexronVI中 | ASTMD471 | 16 | % |
| 质量变化率 | 160°C,504hr,在LubrizolOS206304、5W40中 | ASTMD471 | 17 | % |
| 体积变化 | 150°C,168hr,DexronVI | ASTMD471 | 22 | % |
| 体积变化 | 160°C,504hr,LubrizolOS206304，5W40 | ASTMD471 | 23 | % |
| 玻璃转化温度 | | ASTMD7426 | -37.0 | °C |
| MDR7 | MH:180°C | ASTMD5289 | 16.7 | dNm |
| MDR7 | ML:180°C | ASTMD5289 | 0.820 | dNm |
| MDR7 | PeakRate:180°C | ASTMD5289 | 4.70 | dNm/min |
| MDR7 | tc10:180°C | ASTMD5289 | 43.8 | sec |
| MDR7 | tc50:180°C | ASTMD5289 | 144.0 | sec |
| MDR7 | tc90:180°C | ASTMD5289 | 426.0 | sec |
| MDR7 | Ts2:180°C | ASTMD5289 | 48.6 | sec |
| MooneyScorch-T5(121°C) | | ASTMD1646 | 9.2 | min |
| Resilience | | ISO4662 | 44 | % |
| 挥发性 | | 内部方法 | <0.6 | wt% |