| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 门尼粘度 | 135°C | ASTMD1646 | >12 | MU |
| 门尼粘度 | ML1+4,100°C | ASTMD1646 | 22 | MU |
| 门尼粘度 | 门尼粘度-ML(1+4)(100°C) | ASTMD1646 | 43.6 | um |
| 肖氏硬度2(邵氏A) | | ASTMD2240 | 64 | |
| 拉伸应力2(100%应变) | | ASTMD412 | 7.20 | MPa |
| 抗张强度2(屈服) | | ASTMD412 | 18.2 | MPa |
| 伸长率2(断裂) | | ASTMD412 | 210 | % |
| 压缩永久变形 | 150°C,72hr | ASTMD395 | 22 | % |
| 压缩永久变形 | 150°C,168hr | ASTMD395 | 23 | % |
| 压缩永久变形 | 150°C,1008hr | ASTMD395 | 43 | % |
| 空气中拉伸强度的变化率 | 150°C,168hr | ASTMD573 | 1.0 | % |
| 空气中拉伸强度的变化率 | 100%应变,150°C,168hr | ASTMD573 | 8.0 | % |
| 空气中拉伸强度的变化率 | 150°C,1008hr | ASTMD573 | -5.0 | % |
| 空气中拉伸强度的变化率 | 100%应变,150°C,1008hr | ASTMD573 | 20 | % |
| 空气中极限伸长率的变化率 | 150°C,168hr | ASTMD573 | -1.0 | % |
| 空气中极限伸长率的变化率 | 150°C,1008hr | ASTMD573 | -4.0 | % |
| 空气中硬度计硬度的变化率 | 邵氏A,150°C,168hr | ASTMD573 | 7.0 | |
| 空气中硬度计硬度的变化率 | 邵氏A,150°C,1008hr | ASTMD573 | 9.0 | |
| 拉伸强度的变化率 | 150°C,168hr,在ASTM#1油中 | ASTMD471 | -1.0 | % |
| 拉伸强度的变化率 | 100%应变,150°C,168hr,在ASTM#1油中 | ASTMD471 | 6.0 | % |
| 拉伸强度的变化率 | 150°C,168hr,在SF105油中 | ASTMD471 | -16 | % |
| 拉伸强度的变化率 | 100%应变,150°C,168hr,在SF105油中 | ASTMD471 | -14 | % |
| 拉伸强度的变化率 | 150°C,1008hr,DexronIIIATF | ASTMD471 | -10 | % |
| 拉伸强度的变化率 | 100%应变,150°C,1008hr,DexronIIIATF | ASTMD471 | 12 | % |
| 拉伸强度的变化率 | 150°C,1008hr,在IRM903油中 | ASTMD471 | -41 | % |
| 拉伸强度的变化率 | 100%应变,150°C,1008hr,在IRM903油中 | ASTMD471 | -12 | % |
| 拉伸强度的变化率 | 150°C,1008hr,在SF105油中 | ASTMD471 | -24 | % |
| 拉伸强度的变化率 | 100%应变,150°C,1008hr,在SF105油中 | ASTMD471 | -11 | % |
| 极限伸长率的变化率 | 150°C,168hr,在ASTM#1油中 | ASTMD471 | -10 | % |
| 极限伸长率的变化率 | 150°C,168hr,在SF105油中 | ASTMD471 | -10 | % |
| 极限伸长率的变化率 | 150°C,1008hr,DexronIIIATF | ASTMD471 | -18 | % |
| 极限伸长率的变化率 | 150°C,1008hr,在IRM903油中 | ASTMD471 | -31 | % |
| 极限伸长率的变化率 | 150°C,1008hr,在SF105油中 | ASTMD471 | -20 | % |
| 硬度计硬度的变化率 | 150°C,168hr,在ASTM#1油中 | ASTMD471 | 2.0 | |
| 硬度计硬度的变化率 | 支撐A,150°C,168hr,在SF105油中 | ASTMD471 | -8.0 | |
| 硬度计硬度的变化率 | 150°C,1008hr,在DexronIIIATF中 | ASTMD471 | 0.0 | |
| 硬度计硬度的变化率 | 支撐A,150°C,1008hr,在IRM903油中 | ASTMD471 | -16 | |
| 硬度计硬度的变化率 | 支撐A,150°C,1008hr,在SF105油中 | ASTMD471 | -8.0 | |
| 体积变化 | 150°C,168hr,ASTM标准油（1号） | ASTMD471 | 4.0 | % |
| 体积变化 | 150°C,168hr,在SF105油中 | ASTMD471 | 19 | % |
| 体积变化 | 150°C,1008hr,在10%次氯酸钠中 | ASTMD471 | 16 | % |
| 体积变化 | 150°C,1008hr,在IRM903油中 | ASTMD471 | 44 | % |
| 体积变化 | 150°C,1008hr,在SF105油中 | ASTMD471 | 21 | % |
| 玻璃转化温度 | | ASTMD3418 | -29.0 | °C |
| MDR3 | MH:177°C | ASTMD5289 | 2.61 | J |
| MDR3 | ML:177°C | ASTMD5289 | 0.103 | J |
| MDR3 | Slope:177°C | ASTMD5289 | 6.00 | in-lbs/m.m |
| MDR3 | T50:177°C | ASTMD5289 | 1.1 | min |
| MDR3 | T90:177°C | ASTMD5289 | 3.6 | min |
| MDR3 | Ts2:177°C | ASTMD5289 | 0.5 | min |
| MooneyScorch | t10:135°C | ASTMD1646 | 11.3 | min |
| MooneyScorch | t3:135°C | ASTMD1646 | 8.2 | min |
| TRTest-10 | | ASTMD1329 | -24 | °C |
| 挥发性 | | 内部方法 | <0.4 | wt% |