| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.04 | g/cm3 |
| 熔流率（熔体流动速率） | 200°C/5.0kg | ASTMD1238 | 2.0 | g/10min |
| 熔流率（熔体流动速率） | 220°C/10.0kg | ASTMD1238 | 20 | g/10min |
| 收缩率-流动 | | ASTMD955 | <0.40 | % |
| 吸水率(24hr) | | ASTMD570 | <0.30 | % |
| 抗张强度2(屈服,23°C,3.18mm) | | ASTMD638 | 42.1 | MPa |
| TensileStrength2(Break,23°C,3.18mm) | | ASTMD638 | 35.2 | MPa |
| 伸长率2(断裂,23°C,3.18mm) | | ASTMD638 | 30 | % |
| 弯曲模量3(23°C) | | ASTMD790 | 2550 | MPa |
| 弯曲强度4(屈服,23°C) | | ASTMD790 | 73.5 | MPa |
| 悬壁梁缺口冲击强度 | 23°C,3.18mm | ASTMD256 | 200 | J/m |
| 悬壁梁缺口冲击强度 | 23°C,6.35mm | ASTMD256 | 180 | J/m |
| 洛氏硬度(R计秤,23°C) | | ASTMD785 | 115 | |
| 载荷下热变形温度(1.8MPa,未退火,12.7mm) | | ASTMD648 | 83.0 | °C |
| 维卡软化温度 | | ASTMD15254 | 103 | °C |
| RTIElec(1.6mm) | | UL746 | 60.0 | °C |
| RTIImp(1.6mm) | | UL746 | 60.0 | °C |
| RTIStr(1.6mm) | | UL746 | 60.0 | °C |
| HighAmpArcIgnition(HAI)(1.57mm) | | UL746 | 200 | |
| HighVoltageArcTrackingRate(HVTR)(1.57mm) | | UL746 | 0.00 | mm/min |
| Hot-wireIgnition(HWI)(1.57mm) | | UL746 | 18 | sec |
| FlameRating(1.6mm) | | UL94 | HB | |