| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | | 1.86 | g/cm3 |
| 门尼粘度(ML1+10,121°C) | | | 46 | MU |
| 氟含量 | | | 69 | % |
| 可溶性 | | | LMWKetonesandesters | |
| 肖氏硬度1(邵氏A) | | ASTMD2240 | 78 | |
| 抗张强度2(屈服) | | ASTMD412 | 13.8 | MPa |
| 伸长率3(断裂) | | ASTMD412 | 230 | % |
| 压缩永久变形(200°C,70hr) | | ASTMD395B | 26 | % |
| MH4(177°C) | | | 2.30 | Nm |
| ML5(177°C) | | | 0.240 | Nm |
| t'906(177°C) | | | 2.7 | min |
| ts27(177°C) | | | 1.3 | min |
| 拉伸强度的变化率(23°C,168hr,C级标准燃料) | | ASTMD471 | -30 | % |
| 极限伸长率的变化率(23°C,168hr,C级标准燃料) | | ASTMD471 | -4.0 | % |
| 硬度计硬度的变化率(23°C,168hr,inReferenceFuelC) | | ASTMD471 | -15 | |
| 体积变化(23°C,168hr,C级标准燃料) | | ASTMD471 | 20 | % |