性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
熔融指数 | 200℃,5000g | ASTM D-1238 | 4.6 | g/10min |
比重 | 23℃(73℉) | ASTM D-792 | 1.19 | |
弯曲强度 | 1/8×1×4bar,15mm/min,23℃(73℉) | ASTM D-790 | 715(70.1)(10.17) | kgf/cm |
拉伸强度 | 1/8,50mm/min,23℃(73℉) | ASTM D-638 | 435(42.6)(6.19) | kgf/cm |
弯曲械量 | 1/8×1×4bar,15mm/min,23℃(73℉) | ASTM D-790 | 24000(2.35)(3.41) | kgf/cm |
IZOD冲击强度 | 1/4,6.35mm,23℃(73℉) | ASTM D-256 | 20(196)(3.67) | kgf.cm/cm(J/m)(Ft-lbs/in) |
洛氏硬度 | 23℃(73℉) | ASTM D-785 | 102 | R Scale |
UL燃烧等级 | file NO:E206417 C-UL CSA LS 103112,1/16 | UL 94 | 5VA | |
热变形温度 | 1/2×1/2×5bar,18.6kg/cm | ASTM D-648 | 78(172) | ℃(℉) |
UL燃烧等级 | file NO:E206417 C-UL CSA LS 103112,1/8 | UL 94 | 5VA | |